14CrMoV6-9 High performance special-steels-high resistance industry

14CrMoV6-9

15CDV6, 15CrMoV6, Aerospace series — Steel FE-PL1505 (15CrMoV6) — Air melted — Hardened and tempered — Bars — De ≤ 16mm — 980 MPa ≤ Rm ≤ 1180 MPa

14CrMoV6-9 Datasheet

14CrMoV6-9 High performance special-steels-high resistance industry: DIN EN 10083-1-1991 Chemical composition

C Si Mn P S Cr Mo V Fe
0.11-0.17 ≤0.25 0.80-1.10 ≤0.020 ≤0.015 1.25-1.50 0.80-1.00 0.20-0.30 ≤ ≥

14CrMoV6-9 High performance special-steels-high resistance industry: DIN EN 10083-1-1991 specification

  • DIN EN 10083-1-1991 - Steels for quenching and tempering - Part 1: General technical delivery conditions; German version EN 10083-1:2006

14CrMoV6-9 High performance special-steels-high resistance industry - mechanical properties

Heat treatment Min Max Similar Note
QT > 300 ≤ 50 mm 550
QT > 250 ≤ 300 mm 700
QT ≤250 mm 850
Heat treatment Min Max Similar Note
QT > 250 ≤ 300 mm 700 850
QT > 300 ≤ 50 mm 850 1000
QT ≤250 mm 1000 1300
Heat treatment Min Max Similar Note
QT > 300 ≤ 50 mm 70
QT > 250 ≤ 300 mm 40
QT ≤250 mm 50
Heat treatment Min Max Similar Note
Heat treatment Min Max Similar Note
QT > 300 ≤ 50 mm 12
QT > 250 ≤ 300 mm 11
QT ≤250 mm 10
Heat treatment Type Min Max Similar Note

14CrMoV6-9 is a special steel that was first registered for the first time by Aubert & Duval (known as the famous SCV). In the 80’s, Trafiltubi was the first mill who launched the 15CDV6 in Italy and is already the undisputed specialist in its working. It is the most established and highest performance micro alloy steel for the aviation. Highest purity and excellent mechanical characteristic are coupled with high fatigue resistance, optimal weldability and workability as well as suitability to bending.


14CrMoV6-9 High performance special-steels-high resistance industry delivers